65 HRC Macro Hardness Thermal Spray Coatings HYDROX AP20 For Hydropower manufacturer from China Changzhou Hydraulic Complete Equipment Co., Ltd

65 HRC Macro Hardness Thermal Spray Coatings HYDROX AP20 For Hydropower

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

65 HRC Macro Hardness Thermal Spray Coatings HYDROX AP20 For Hydropower

Description:

Anti-corrosion and salt spray test > 4000hrs

Macro hardness 65 HRC

Maximum temperature 540C

Bond strength > 40MPa

Standard: ASTM-C633 ,NEN-EU 5,NEN-ISO 4287,NEN-ISO 4287,ASTM D2794-93

NEN-ISO 4287,DIN50021-155,TNOCA02.8043

HYDROX AP20 Coating Technical Specifications

List of items	HYDROX AP20	Standard
List of items	HYDROX AP20	Standard
Typical coating composition	Inc625-Cr2O3TiO2
Coating thickness	Bottom ( Inc625) ≥150um
	Surface layer ( Cr2O3TiO2) ≥200um
Bond strength	> 40MPa	ASTM-C633
Maximum temperature	540C
Porosity	< 2%
Macro hardness	65 HRC
Micro hardness	> 1000HV200	NEN-EU 5
Surface Finish (Ra)	0.15um-0.4um	NEN-ISO 4287
Surface Finish (Rz)	< 4.5um	NEN-ISO 4287
Shock Value	> 2J	ASTM D2794-93
RPK Material contact area	> 80%,Depth 1,0um	NEN-ISO 4287
Anti-corrosion and salt spray test	> 4000hrs	DIN50021-155
ECP(Drying)	< -350mV
ECP(Semi-dry)	< -350mV	TNOCA02.8043
ECP(Wet)	< -350mV

To apple ceramic coating on the equipment surface can have many benefits . Such as high hardness, high temperature resistant, corrosion resistance, salt fog resistance. Effect is much better than common electroplating. It works well in ocean industry, food machinery, water conservancy and hydropower, aerospace and other industries.

Thermal Ceramic coated piston rod Spray Coatings